Activated Alumina
Molecular Sieves
Tower Packing
Activated Carbon
Silica Gel
Click the number：5978 Entry time：2015/2/27 【Print this page】 【Close】
Type A Silica Gel
Type A Silica Gel
中文名：A型硅胶
Molecular formula: xSiO2·yH2O
Molecular weight: 60.08
Sizes: 0.5-1.5mm, 0.5-1mm, 1-3mm, 2-4mm, 3-5 mm, 4-8mm
Type A silica gel also called Fine-pored silica gel
Specifications
|
Item |
Unit |
Type 1 |
Type 2 |
|
|
Appearance |
|
Transparent, translucent, glass-like pellet or lump |
||
|
Adsorption capacity |
RH=20% |
% |
≥11 |
≥11 |
|
RH=50% |
% |
≥25 |
≥25 |
|
|
RH=90% |
% |
≥37 |
≥37 |
|
|
Loss on heating |
% |
≤2 |
≤5 |
|
|
PH value |
|
4 |
4 |
|
|
Specific resistance |
Ω.cm |
≥4000 |
≥4000 |
|
|
Silica |
% |
≥98.5 |
≥98.5 |
|
|
Qualified ratio of spherical granules |
% |
≥90 |
≥90 |
|
|
Size |
mm |
2-5mm |
2-5mm |
|
|
Bulk density |
g/l |
780 |
780 |
|
|
Average pore diameter |
nm |
2.0-3.0 |
2.0-3.0 |
|
|
Specific surface area |
m2/g |
650-800 |
650-800 |
|
|
Pore volume |
ml/g |
0.35-0.45 |
0.35-0.45 |
|
|
Specific heat |
KJ/kg.℃ |
0.92 |
0.92 |
|
|
Thermal conductivity |
KJ/m.hr.℃ |
0.63 |
0.63 |
|
|
The moisture content, packing and size may be customized per your specific requirements |
||||
Packing
25kgs/bag or 500kgs/bag
Application
Mainly used for drying and moistureproof, may also be used as catalyst carriers, adsorbents, separators and variable pressure adsorbents, etc.
Introduction
Silica gel is transparent or ivory-white granular solid, main ingredients are amorphous silica. Silica gel does not dissolve in water and any solvents, non-toxic tasteless, not burning. Silica gel has stable chemical properties, does not react with any material except the strong alkali, hydrofluoric acid. Silica gel has open porous structure, high adsorption properties, good thermal stability, stable chemical properties, high mechanical strength, etc.
Added dilute sulfuric acid (hydrochloric acid) into the aqueous solution of sodium silicate and let standing, thus becoming solid aqueous silicate gel. Used water washing to remove Na+ and SO4 2- (Cl-) ions dissolved in the electrolyte, after drying it is silica gel. Different manufacturing methods form different microporous structure, different microporous structure form different models, such as macroporous silica gel, silochrom (type C silica gel), type B silica gel, fine-pored silica gel (type A silica gel).
Silica gel used for gas drying, gas absorption, liquid dehydration, chromatography, catalysts, etc.
Regeneration temperature
Silica gel can be removed moisture by the way of thermal desorption, desorption temperatures as follows:
Type C silica gel≤600℃
Type A silica gel≤200℃
Allochroic silica gel≤120℃
Silica alumina gel≤350℃